ʻO ka mea kino bakeke o wY25 excavator ʻo Q345, nona ka weldability maikaʻi. ʻO ka mea niho bakeke ʻo ZGMn13 (ke kila manganese kiʻekiʻe), ʻo ia ka austenite hoʻokahi-phase i ke kiʻekiʻe o ka wela a me ka paʻakikī maikaʻi a me ke kūpaʻa kiʻekiʻe o ka lole ma lalo o ke kaumaha o ka hopena ma muli o ka paʻakikī o ka hana o ka papa honua. Akā, ʻilihune kēia kila weldability: kekahi i loko o ka welding wela-pili wahi precipitation o carbide ma muli o ka mea embrittlement; ʻO ka lua, ʻo ka weld thermal cracking, ʻoi aku ma kahi kokoke i kahi seam zone liquefaction crack.
1.heat-hopena wahi ua carbide ma muli o ka embrittlement
Hiki i ka ZGMn13 ke kila manganese kiʻekiʻe ke hoʻoheheʻe i ka carbide ma ka palena o ka palaoa i ka wā e wela hou ai ma mua o 250 ℃, no laila e hoʻemi nui ʻia ka paʻakikī o ka mea a me ka hana maikaʻi loa o ke kila manganese kiʻekiʻe. Ma hope o ka nānā ʻana, i ka wā e wela hou ai ke kila manganese kiʻekiʻe a ʻoi aku ka wikiwiki o ka hoʻomaha ʻana, e hoʻomaka mua ka carbide i ka palena o ka palaoa, a me ka hoʻonui ʻana i ka manawa noho, e hoʻololi ka carbide ma ka palena o ka palaoa mai ka mokuʻāina discontinuous a mesh. e hoʻohelehele ʻia, a e hoʻonui nui ʻia kona palupalu. No laila, i ka wā o ke kila manganese kiʻekiʻe i ka welding a reheating ma hope o ka welding, e i loko o ka welding wela-pili wahi o ka pauku o ka precipitation o carbide i nā degere likeʻole, a hiki ke martensitic hoʻololi,ʻaʻole wale e hana i ka mea brittle, akā, no hoi. e ho'ēmi i kona pale lole a me ka paʻakikī. A, i loko o ka wela-pili wahi maʻalahi e precipitate carbide pae wela (650 ℃ a pela aku) i ka lōʻihi o ka noho manawa, oi ka carbide precipitation.
I mea e hōʻemi ai i ka ua o ka carbide a pale aku i ka waiwai mai ka lilo ʻana i ka paʻakikī a lilo i brittle, pono e lawe ʻia nā ana e hoʻolōʻihi i ka pae hoʻomaha, ʻo ia hoʻi, e hoʻopōkole i ka manawa noho i nā wela kiʻekiʻe. No kēia kumu, ʻo ka excavator bakeke kino a me ka bakeke niho wiliwili e hoʻohana i ka pōkole pauku kuʻihao, intermittent kuʻi, soaking wai kuʻihao, etc.
2.Welding thermal māwae
ʻO ka pale ʻana i ka haʻihaʻi wela ka mea e hōʻemi ai i ka ʻike o S a me P i loko o ka metala kumu a i ʻole nā mea weld; hiki nō hoʻi ke hana i nā mea e hoʻemi ai i ke koʻikoʻi o ka welding mai ke kaʻina hana hoʻoheheʻe, e like me ka hoʻohana ʻana i ka welding pauku pōkole, ka wiliwili intermittent, dispersion welding a me ka hammering ma hope o ka wili. I loko o ke kino bākeke overlay wiliwili kiʻekiʻe manganese kila, e hiki mua weld i ka papa o Cr-ni, Cr-ni-Mn a Cr-Mn austenitic kila no ka hoʻokaʻawale kuʻihao ala, hiki ke pale i ka pohā.
Ke kaʻina hana wiliwili ʻana i ke kino o ka bakeke Excavator a me ka bakeke niho
1.Preparation ma mua o ka wili
ʻO ka mea mua, e wehe i nā niho o ka bākeke mai ke kino o ka bākeke, a laila e hoʻohana i ka mīkini kihi e hoʻomaʻemaʻe i ka hoʻokomo ʻana i nā niho bakeke maʻemaʻe, ʻaʻohe lepo, ʻōpala, a nānā pono inā he mau māwae a me nā hemahema ʻē aʻe; wehe i ka bevel me carbon arc kinoea planer ma ka bakeke niho e welded, a hoʻomaʻemaʻe me ka angle grinder.
2.Welding
① mua i loko o ke kino bākeke (a me nā ami niho bākeke) me GBE309-15 welding electrodes no ka overlay welding, pono nā electrodes wili i 350 ℃, 15h maloʻo ma mua o ka hoʻomaloʻo ʻana, nui ka nui o ka welding, ʻoi aku ka lohi o ka welding e hōʻoia ai ka fusion zone nickel maʻiʻo o 5% a 6%, e pale i ka hana ʻana o ka martensite maʻalahi.
② E hana i ka wili hoʻonohonoho. Ma hope o ka hōʻuluʻulu ʻia ʻana o nā niho bākeke ma kahi, hoʻohana ʻia ke koʻokoʻo wiliwili D266 me ke anawaena o 32MM no ka hoʻonohonoho hoʻonohonoho hoʻohālikelike ma nā ʻaoʻao ʻelua, ʻaʻole ʻoi aku ka lōʻihi o ka weld ma mua o 30MM. ka hoʻoluʻu wai a me ka hāmare ma hope koke o ka wili ʻana.
③Kuowili lalo. E hoʻohana i ke koʻokoʻo wiliwili 32MM anawaena D266 no ka wiliwili ʻana i lalo. E hoʻohana i ka haʻahaʻa o kēia manawa, DC reverse polarity, intermittent welding.